Fatigue crack growth behaviour of Inconel 718 - The concept of a damaged zone caused by high temperature hold times
Paper i proceeding, 2011

Fatigue crack growth testing of Inconel 718 has been carried out at the temperatures 550°C and 650°C. The tests were conducted using a mix of hold times and pure cyclic loading, referred to as block tests. From the test results, the existence of an embrittled volume or damaged zone in the vicinity of the crack tip has been revealed. It has been found that the evolution of this damaged zone can be sufficiently well described using a power law function with an exponent n=0.25. © 2011 Published by Elsevier Ltd.

Fatigue crack propagation

Inconel 718

Hold times

Nickel-base superalloys

Grain boundary embrittlement

Författare

David Gustafsson

J.J. Moverare

K. Simonsson

S.A.H. Johansson

Magnus Hörnqvist

T. Månsson

S. Sjöström

Procedia Engineering

1877-7058 (ISSN)

Vol. 10 2821-2826

Ämneskategorier

Maskinteknik

Materialteknik

DOI

10.1016/j.proeng.2011.04.469

Mer information

Senast uppdaterat

2018-10-15