Fabrication and investigation of YBa2Cu3O7-delta/Ba0.05Sr0.95TiO3 thin film structures for voltage tunable devices
Artikel i vetenskaplig tidskrift, 1998

High-temperature superconducting/ferroelectric thin film structures were deposited by laser ablation. Three types of voltage tunable devices were fabricated and investigated-trilayer capacitor, planar interdigital capacitor and coplanar waveguide. As ferroelectric the solid solution BaxSr1-xTiO3 was chosen with barium content x = 0.05 because its Curie temperature is close to the liquid nitrogen boiling point (77 K). Temperature and voltage dependences of the Ba0.05Sr0.95TiO3 dielectric constant epsilon(r,BSTO) were studied. High epsilon(r,BSTO) values were determined-up to 3000 at 75 K, 20 GHz and zero de bias. Efficient voltage tunability was demonstrated (up to 40%) at loss level tan delta=0.01-0.1. Compact YBa2Cu3O7-delta/Ba0.05Sr0.95TiO3 coplanar waveguide with as narrow gap as 18 mu m was tested as electrically tunable phase-shifter and field-induced phase shifts of more than 180 degrees were obtained by 35 V de bias at 20 GHz. This improvement was attained by proper choice of the ferroelectric material, accomplished epitaxial growth of the films and decrease of the specific dimensions. (C) 1998 Published by Elsevier Science B.V. All rights reserved.

voltage tunable devices

thin film

laser ablation

Författare

R Chakalov

Zdravko Ivanov

Institutionen för fysik

Peter Larsson

Institutionen för mikroelektronik och nanovetenskap

Erik F. Carlsson

Institutionen för mikrovågsteknik

Spartak Gevorgian

Institutionen för mikroelektronik och nanovetenskap

Tord Claeson

Fysiska institutionen

Physica C: Superconductivity and its Applications

0921-4534 (ISSN)

Vol. 308 3-4 279-288

Ämneskategorier

Fysik

Den kondenserade materiens fysik

Mer information

Skapat

2017-10-06