Elastically strained and relaxed La0.67Ca0.33MnO3 films grown on lanthanum aluminate substrates with different orientations
Artikel i vetenskaplig tidskrift, 2016

Structure of 40-nm thick La0.67Ca0.33MnO3 (LCMO) films grown by laser evaporation on (001) and (110) LaAlO3 (LAO) substrates has been investigated using the methods of medium-energy ion scattering and X-ray diffraction. The grown manganite layers are under lateral biaxial compressive mechanical stresses. When (110)LAO wafers are used as the substrates, stresses relax to a great extent; the relaxation is accompanied by the formation of defects in a (3-4)-nm thick manganite-film interlayer adjacent to the LCMO-(110)LAO interface. When studying the structure of the grown layers, their electro- and magnetotransport parameters have been measured. The electroresistance of the LCMO films grown on the substrates of both types reached a maximum at temperature T (M) of about 250 K. At temperatures close to T (M) magnetoresistance of the LCMO/(110)LAO films exceeds that of the LCMO/(001)LAO films by 20-30%; however, the situation is inverse at low temperatures (T < 150 K). At T < T (M) , the magnetotransport in the grown manganite films significantly depends on the spin ordering in ferromagnetic domains, which increase with a decrease in temperature.

energy ion-scattering

perovskite

single-crystals

microstructure

magnetic-properties

transition

transport

anisotropic magnetoresistance

thin-films

magnetotransport

Författare

Y. A. Boikov

Russian Academy of Sciences

I.T. Serenkov

Russian Academy of Sciences

V.I. Sakharov

Russian Academy of Sciences

Tord Claeson

Chalmers, Mikroteknologi och nanovetenskap (MC2), Kvantkomponentfysik

Physics of the Solid State

1063-7834 (ISSN) 1090-6460 (eISSN)

Vol. 58 12 2560-2566

Ämneskategorier

Fysik

DOI

10.1134/s1063783416120039

Mer information

Senast uppdaterat

2018-07-04