Influence of dwell time on fatigue crack propagation in Alloy 718 laser welds
Artikel i vetenskaplig tidskrift, 2017

The introduction of welded assemblies in aerospace components aid in weight reduction, but also lead to an increased risk of defects. It is therefore important to analyze the high temperature crack growth resistance of such welds. The results from high temperature cyclic and dwell-fatigue testing of surface flawed Alloy 718 welds are presented here. An increasing temperature and application of a dwell time accelerate the crack growth and increase interaction with secondary phases. During cyclic loading at 550 °C, there is little interaction with the microstructure during transgranular propagation, but the application of dwell times results in a mixture of transgranular propagation and intergranular cracking of boundaries between different dendrites. At 650 °C, mixed intergranular and transgranular mode of crack growth is seen under both cyclic and dwell conditions. However, during dwell-fatigue the interfaces between the secondary arms of the same dendrite are also weakened, leading to an interfacial type of crack growth also in the intergranular parts.

Nickel superalloys

Laser welds

Electron microscopy

Crack growth

EBSD

Dwell-fatigue

Författare

Anand Harihara Subramonia Iyer

Chalmers, Fysik, Materialens mikrostruktur

Krystyna Marta Stiller

Chalmers, Fysik, Biologisk fysik

Chalmers, Fysik, Materialens mikrostruktur

Gunnar Leijon

Swerea KIMAB

Henrik C.M. Andersson-Östling

Swerea KIMAB

Magnus Hörnqvist Colliander

Chalmers, Fysik, Materialens mikrostruktur

Materials Science & Engineering A: Structural Materials: Properties, Microstructure and Processing

0921-5093 (ISSN)

Vol. 704 440-447

Ämneskategorier

Metallurgi och metalliska material

Infrastruktur

Chalmers materialanalyslaboratorium

Styrkeområden

Materialvetenskap

DOI

10.1016/j.msea.2017.08.049

Mer information

Senast uppdaterat

2018-11-07