Microstructural evolution of welded stainless steels on integrated effect of thermal aging and low flux irradiation
Paper i proceeding, 2018

The combined effect of thermal aging and irradiation on cast and welded stainless steel solidification structures is not sufficiently investigated. From theory and consecutive aging and irradiation experiments, the effect of simultaneous low rate irradiation and thermal aging is expected to accelerate and modify the aging processes of the ferrite phase. Here, a detailed analysis of long-term aged material at very low fast neutron flux at LWR operating temperatures using Atom Probe Tomography is presented. Samples of weld material from various positions in the core barrel of the Zorita PWR are examined. The welds have been exposed to 280–285 °C for 38 years at three different neutron fluxes between 1 × 10 −5 and 7 × 10 −7 dpa/h to a total dose of 0.15–2 dpa. The aging of the ferrite phase occurs by spinodal decomposition, clustering and precipitation of e.g. G-phase. These phenomena are characterized and quantitatively analyzed in order to understand the effect of flux in combination with thermal aging.

Spinodal decomposition

Weld ferrite

Stainless steel

Irradiation

Thermal aging

Författare

Martin Bjurman

Studsvik

Kungliga Tekniska Högskolan (KTH)

Kristina Lindgren

Chalmers, Fysik, Materialens mikrostruktur

Mattias Thuvander

Chalmers, Fysik, Materialens mikrostruktur

Peter Ekström

Strålsäkerhetsmyndigheten (SSM)

P. Efsing

Kungliga Tekniska Högskolan (KTH)

Ringhals AB

Minerals, Metals and Materials Series

2367-1181 (ISSN) 2367-1696 (eISSN)

Vol. Part F11 703-710

18th International Conference on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors
Portland, USA,

Ämneskategorier

Bearbetnings-, yt- och fogningsteknik

Annan materialteknik

Metallurgi och metalliska material

DOI

10.1007/978-3-319-68454-3_54

Mer information

Senast uppdaterat

2018-03-28