Effect of water vapor on the oxidation behavior of HVAF-sprayed NiCr and NiCrAlY coatings
Artikel i vetenskaplig tidskrift, 2018

Isothermal oxidation behavior of NiCr and NiCrAlY coatings deposited onto low alloy 16Mo3 steel by high-velocity air fuel (HVAF) process was investigated in 5% O-2+20% H2O+N-2 at 600 degrees C for 168h. Whereas NiCrAlY showed lower mass gain compared to NiCr, both coatings succeeded in maintaining the integrity with the substrate during the exposure without any breakaway oxidation. A thin Cr-rich oxide scale (Cr2O3) formed on NiCr, and a thin mixed oxide scale (Al2O3 with NiCr2O4) formed on NiCrAlY significantly increasing the oxidation protection in the presence of water vapor.

NiCr

water vapor

oxidation protection

NiCrAlY

thermal spray coating

Författare

Esmaeil Sadeghimeresht

Högskolan Väst

Johan Eklund

Chalmers, Kemi och kemiteknik, Energi och material, Oorganisk miljökemi

Julien Phother Simon

Chalmers, Kemi och kemiteknik, Energi och material, Oorganisk miljökemi

Jesper Liske

Chalmers, Kemi och kemiteknik, Energi och material, Oorganisk miljökemi

Nicolaie Markocsan

Högskolan Väst

Shrikant Joshi

Högskolan Väst

Materials and Corrosion - Werkstoffe und Korrosion

0043-2822 (ISSN) 1521-4176 (eISSN)

Vol. 69 10 1431-1440

Ämneskategorier

Bearbetnings-, yt- och fogningsteknik

Metallurgi och metalliska material

Korrosionsteknik

DOI

10.1002/maco.201710005

Mer information

Senast uppdaterat

2019-01-07