Conduction mechanism in polymeric membranes based on PEO or PVdF-HFP and containing a piperidinium ionic liquid
Artikel i vetenskaplig tidskrift, 2019

Two types of polymer electrolyte membranes were prepared using poly(ethylene oxide) (PEO) and poly(vinylidene difluoride-co-hexafluoropropylene) (PVdF-HFP), with different amounts of the ionic liquid N-methyl-N-propylpiperidinium bis(trifluoromethane-sulfonyl) imide ([PP13][TFSI]) added. The results from differential scanning calorimetry and conductivity measurements show that in the case of PVdF-HFP membranes the glass transition temperature T-g decreases and the room temperature ionic conductivity increases with increasing content of the ionic liquid (up to 60 wt.%). However, in the case of PEO based membranes Tg is less significantly affected and the room temperature ionic conductivity increases only up to 30 wt.% of ionic liquid, beyond which a steady value of about 5.10(-5) S/cm is reached. The results from Raman spectroscopy show that the characteristic vibrational mode of the TFSI anion at similar to 742 cm(-1) is weakly affected in the membranes prepared from PVdF-HFP, whereas for those based on PEO it has a clearer composition dependence. These results suggest ion-ion and ion-polymer interactions of different nature, which together with the different nanomorphologies adopted by PEO and PVdF-HFP, as revealed by X-ray scattering, give rise to different composition dependences of the macroscopically measured ionic conductivity. (C) 2019 The Authors. Published by Elsevier Ltd.

Poly(vinylidene difluoride-co-hexafluoropropylene)

Poly(ethylene oxide)

Ionic liquid and ionic conductivity

Författare

Khalid Elamin

Chalmers, Kemi och kemiteknik, Tillämpad kemi, Anna Martinelli Group

Mansoureh Shojaatalhoseini

Chalmers, Fysik, Kondenserade materiens fysik

Olesia Danyliv

Chalmers, Kemi och kemiteknik, Tillämpad kemi, Anna Martinelli Group

Anna Martinelli

Chalmers, Kemi och kemiteknik, Tillämpad kemi, Anna Martinelli Group

Jan Swenson

Chalmers, Fysik, Biologisk fysik

Electrochimica Acta

0013-4686 (ISSN)

Vol. 299 979-986

Ämneskategorier

Oorganisk kemi

Keramteknik

Materialkemi

DOI

10.1016/j.electacta.2018.12.154

Mer information

Senast uppdaterat

2019-02-28