TRANSVERSE MODULUS MEASUREMENT OF CARBON FIBRE BY ATOMICE FORCE MICROSCOPE AND NANOINDENTATION
Paper i proceeding, 2019

Carbon fibre reinforced polymer composite has been widely used in structural component due to the high specific axial modulus of carbon fibre. However, the transverse Young’s modulus is much lower and not well studied because of the extremely small diameter (~5 μm). In this work, flat test surfaces on carbon fibre IMS65 were fabricated using focused ion beam. The transverse Young’s modulus was measured by nano-scale indentation tests, which were performed on fabricated flat surfaces, using both atomic force microscopy and nano-indentation. The surface damage induced by the high energy ion beam was also assessed.

Transverse Young’s modulus

AFM

FIB-SEM

Carbon fibre

Nano-indentation

Författare

Duan Shanghong

Chalmers, Industri- och materialvetenskap, Material- och beräkningsmekanik

Fang Liu

Chalmers, Industri- och materialvetenskap, Material och tillverkning

Torbjörn Pettersson

Kungliga Tekniska Högskolan (KTH)

Claudia Creighton

Deakin University

Leif Asp

Chalmers, Industri- och materialvetenskap, Material- och beräkningsmekanik

TWENTY-SECOND INTERNATIONAL CONFERENCE ON COMPOSITE MATERIALS (ICCM22)
Melbourne, Australia,

SORCERER

Europeiska kommissionen (Horisont 2020), 2017-02-01 -- 2020-02-28.

Skadetålighet hos strukturella batterier

Amerikanska flygvapnets kontor för strategisk forskning (AFOSR), 2017-09-30 -- 2020-09-29.

Ämneskategorier

Teknisk mekanik

Nanoteknik

Kompositmaterial och -teknik

Den kondenserade materiens fysik

Infrastruktur

Chalmers materialanalyslaboratorium

Styrkeområden

Materialvetenskap

Mer information

Senast uppdaterat

2019-08-28