Highly Stable Fe3O4/C Composite: A Candidate Material for All Solid-State Lithium-Ion Batteries
Artikel i vetenskaplig tidskrift, 2020

Fe3O4 nanoparticles synthesized by a base catalyzed method are tested in an All-Solid-State (ASLB) battery using a sulfide electrolyte. The pristine nanoparticles were morphologically characterized showing an average size of 12 nm. The evaluation of the electrochemical properties shows high specific capacity values of 506 mAhg(-1) after 350 cycles at a specific current of 250 mAg(-1), with very high stability and coulombic efficiency. (C) 2020 The Author(s). Published on behalf of The Electrochemical Society by IOP Publishing Limited.

Författare

F. Maroni

Universita degli Studi Gabriele d'annunzio di Chieti-Pescara

P. Bruni

Universita degli Studi Gabriele d'annunzio di Chieti-Pescara

N. Suzuki

Samsung R&D Inst Japan

Y. Aihara

Samsung R&D Inst Japan

S. Gabriella

Universita degli Studi di Camerino

G. Carbonari

Universita degli Studi di Camerino

Marco Agostini

Chalmers, Fysik, Materialfysik

M. Branchi

Sapienza, Università di Roma

S. Ferrari

Universita degli Studi Gabriele d'annunzio di Chieti-Pescara

M. A. Navarra

Sapienza, Università di Roma

S. Brutti

Sapienza, Università di Roma

Aleksandar Matic

Chalmers, Fysik, Materialfysik

F. Nobili

Universita degli Studi di Camerino

F. Croce

Universita degli Studi Gabriele d'annunzio di Chieti-Pescara

Journal of the Electrochemical Society

0013-4651 (ISSN)

Vol. 167 7 070556

Ämneskategorier

Den kondenserade materiens fysik

DOI

10.1149/1945-7111/ab80ce

Mer information

Senast uppdaterat

2020-09-03