The Nanostructure of the Oxide Formed on Fe-10Cr-4Al Exposed in Liquid Pb
Artikel i vetenskaplig tidskrift, 2022

An Fe-10Cr-4Al alloy containing reactive elements developed for application in high-temperature liquid lead environments was analyzed after exposure in 600 and 750°C lead with dissolved oxygen for 1,000-2,000 h. Atom probe tomography, transmission electron microscopy, and X-ray scattering were all used to study the protective oxide formed on the surface. Exposure at 750°C resulted in a 2-μm thick oxide, whereas the 600°C exposure resulted in a 100-nm thick oxide. Both oxides were layered, with an Fe-Al spinel on top, and an alumina layer toward the metal. In the 600°C exposed material, there was a Cr-rich oxide layer between the spinel and the alumina. Metallic lead particles were found in the inner and middle parts of the oxide, related to pores. The combination of the experimental techniques, focusing on atom probe tomography, and the interpretations that can be done, are discussed in detail.

FeCrAl

oxide

reactive elements

liquid lead

atom probe tomography

Författare

Kristina Lindgren

Chalmers, Fysik, Mikrostrukturfysik

Peter Dömstedt

Kungliga Tekniska Högskolan (KTH)

Peter Szakalos

Kungliga Tekniska Högskolan (KTH)

Mattias Thuvander

Chalmers, Fysik, Mikrostrukturfysik

Microscopy and Microanalysis

1431-9276 (ISSN) 1435-8115 (eISSN)

Vol. 28 4 1321 -1334

Ämneskategorier

Oorganisk kemi

Materialkemi

Korrosionsteknik

Drivkrafter

Hållbar utveckling

Styrkeområden

Energi

Materialvetenskap

Infrastruktur

Chalmers materialanalyslaboratorium

DOI

10.1017/S1431927621000337

PubMed

33888175

Mer information

Senast uppdaterat

2022-08-08