Development and characterisation of nanofiber films with high adhesion
Paper i proceeding, 2011

With the development of thermal management, thermal interface material (TIM) plays a more and more important role in electronic packaging. This paper reports the study on fabrication of a nanofiber films used for nano-thermal interface material (nano-TIM) with the adhesive function. The nano-TIM with high thermal conductivity and low thermal resistivity has been fabricated by electrospinning process. In the present work, hotmelt was added into the electrospinning solution to improve the adhesion properties of the film. The morphology of the film was observed by Scanning Electrical Microscope (SEM). The nanofiber films have a nano-scale structure with hotmelt randomly attached into the fiber matrix. Shear tests were conducted to measure the bonding strength of nanofiber films. The results show that the nanofiber films reached a 6.52 MPa in terms of average shear strength, more than 2 times better than the case without the hotmelt addition. © 2011 IEEE.

Författare

X. Tang

Shanghai University

H. Cui

Shanghai University

Xiuzhen Lu

Shanghai University

Q. Fan

Shanghai University

Zhichao Yuan

Shanghai University

L. Ye

Shanghai University

Johan Liu

SHT Smart High-Tech

Chalmers, Teknisk fysik, Elektronikmaterial och system

Shanghai University

Proceedings - Electronic Components and Technology Conference

05695503 (ISSN)

673-677 5898586

2011 61st Electronic Components and Technology Conference, ECTC 2011
, USA,

Styrkeområden

Nanovetenskap och nanoteknik (SO 2010-2017, EI 2018-)

Materialvetenskap

Ämneskategorier

Polymerteknologi

Textil-, gummi- och polymermaterial

Kompositmaterial och -teknik

DOI

10.1109/ECTC.2011.5898586

Mer information

Senast uppdaterat

2021-08-12