Highly Reliable Yarn-Type Supercapacitor Using Conductive Silk Yarns with Multilayered Active Materials
Artikel i vetenskaplig tidskrift, 2021

The fibrous supercapacitor is a promising candidate for wearable energy-storage systems due to excellent mechanical reliability under deformation. In this study, a mechanically reliable fibrous supercapacitor with high volumetric power density and energy density was developed using fiber electrodes composed of multilayered active materials coated on silk yarns. The conductive silk yarn electrodes are fabricated via a sequential dip-coating process of silver nanowires, multi-walled carbon nanotubes (MWCNT, three to seven walls), and poly(3,4-ethylenedioxythiophene):poly(styrene sulfonate) (PEDOT:PSS). The composite-coated silk yarn electrodes were stable under cyclic bending as well as under washing in water. Due to the synergetic effect of the three conducting materials, an excellent electrochemical performance was obtained resulting in high volumetric energy and power densities of 8–13 mWh cm−3 and 8–19 W cm−3, respectively. A yarn-type supercapacitor was demonstrated by integrating composite-coated silk yarn electrodes with a hydrogel electrolyte, showing a promising stability as evidenced by the retention of over 94% and 93% of the specific capacitance after 90-degree bending and stretching.

silk

silver nanowires

Multilayer

supercapacitor

carbon nanotubes

Författare

Youngjae Seo

Chung-Ang University

Heebo Ha

Chung-Ang University

Jun Young Cheong

Samsung SDI

Korea Advanced Institute of Science and Technology (KAIST)

Mirine Leem

Sungkyunkwan University

Sozan Darabi

Chalmers, Kemi och kemiteknik, Tillämpad kemi, Christian Müller Group

Paolo Matteini

Istituto Di Fisica Applicata Nello Carrara

Christian Müller

Chalmers, Kemi och kemiteknik, Tillämpad kemi, Christian Müller Group

Tae Gwang Yun

Myongji University

Byungil Hwang

Chung-Ang University

Journal of Natural Fibers

1544-0478 (ISSN) 1544-046X (eISSN)

Vol. In Press

Ämneskategorier

Materialkemi

Annan kemi

Kompositmaterial och -teknik

DOI

10.1080/15440478.2021.1993509

Mer information

Senast uppdaterat

2021-11-15