Defect-engineered metal-organic frameworks (MOF-808) towards the improved adsorptive removal of organic dyes and chromium (vi) species from water

Khoa D. Nguyen; Nhi T. Vo; Khanh T.M. Le; Khanh V. Ho; Nam T.S. Phan; Hoang Phuoc Ho; Ha V. Le

doi:10.1039/d2nj05693c

Defect-engineered metal-organic frameworks (MOF-808) towards the improved adsorptive removal of organic dyes and chromium (vi) species from water
Artikel i vetenskaplig tidskrift, 2023

In this work, two defective zirconium-based metal-organic frameworks (Zr-MOFs), MOF-808-OH and MOF-808-NH2, were synthesized by partially replacing the 1,3,5-benzenetricarboxylate building block with 5-hydroxyisophthalate and 5-aminoisophthalate, respectively. The structural features of the defective materials were analyzed by powder X-ray diffraction (PXRD), scanning electron microscopy (SEM), nitrogen physisorption at 77 K, and thermogravimetric analysis (TGA). Importantly, the number of defect sites determined via proton nuclear magnetic resonance (1H-NMR) analysis of the digested materials was approximately 7 mol% for MOF-808-OH and 3 mol% for MOF-808-NH2. The presence of the defect sites increased the number of acidic centers on Zr-clusters originating from missing-linker nodes which accounted for a remarkable adsorption capacity towards various anionic organic dyes and chromium (vi) species. Compared to standard MOF-808, the defect-engineered ones showed significant increments by 30-60% in trapping capacity for anionic contaminants including sunset yellow, quinoline yellow, methyl orange, and potassium dichromate, while they exhibited modest improvements by 5-15% in the removal of cationic dyes, namely malachite green and methylene blue.