High-temperature corrosion of weld overlay coating/bulk FeCrAl exposed in O2 + H2O + KCl(s) at 600 °C – A microstructural investigation

Artikel i vetenskaplig tidskrift, 2023

This work investigates the impact of high-temperature corrosion behavior of the newly developed FeCrAl alloy Kanthal® EF101 bulk material and weld overlay coating in the presence of KCl(g)/KCl(s) at 600 °C. The oxide scale formed within the secondary corrosion regime after exposure and the impact of alloy microstructure on corrosion behavior was investigated using scanning transmission electron microscopy. The findings indicated the key microstructural differences is the alloy grain size which influences the formation of a protective scale. In addition, It is indicated that coating exhibited inferior performance than the bulk material, primarily attributed to the microstructural differences.