Alkali Induced High Temperature Corrosion of Stainless Steel - Experiences from Laboratory and Field
Doktorsavhandling, 2008

The high temperature corrosion of steam superheaters is a major obstacle that has to be overcome in order to increase the electricity generating efficiency of power boilers burning biomass or waste. This thesis addresses this issue by a combination of well-controlled model experiments in the laboratory and short and long term field exposures using cooled probes in full-scale biomass and waste fired boilers. The work primarily concerns the effect of alkali salts such as KCl, K2CO3 and K2SO4 on the high temperature corrosion of 304L type stainless steel (Fe18Cr10Ni). The laboratory experiments show that KCl and K2CO3 strongly accelerate the high temperature corrosion of 304L steel. The two salts react with the chromium rich oxide on the sample surface, forming K2CrO4. The formation of chromate(VI) is a sink for chromium in the oxide and leads to a loss of its protective properties. This result in rapid oxide growth and the formation of a thick duplex scale consisting of an outer hematite (Fe2O3) layer with scattered potassium chromate particles on top and an inner layer consisting of FeCrNi spinel-type oxide. This scale shows striking similarities with the duplex scale developed on 304L in O2 + H2O in the absence of salt. This corrosion morphology is referred to as “Type A”. The duplex scale is relatively poorly protective and can be penetrated by chloride ions, resulting in the formation of transition metal chlorides at the metal/oxide interface. In contrast to KCl and K2CO3, K2SO4 does not react with chromium in the oxide to form chromate. This explains why potassium sulphate does not cause accelerated corrosion of 304L. Exposure in the presence of KCl also resulted in another type of corrosion (“Type B”) with corrosion product agglomerates (mainly iron oxide) forming at the KCl crystallites. The oxide agglomerations are not associated with a localized attack of the steel. Hence, “Type B” corrosion is considered to be of secondary importance. Several field exposures were performed in order to investigate if corrosion in commercial boilers can be mitigated by sulphur-containing additives to the fuel. Using cooled probes, the addition of sulphur was shown to decrease corrosion rate by 50%. Adding sulphur to the fuel completely suppressed the formation of chromate(VI) and decreased the amount of transition metal chlorides on the samples. The mitigation of corrosion is attributed to the conversion of alkali chloride to alkali sulphate in the flue gas and in the deposits. The results imply that the “chromate formation” mechanism is important for superheater tubes in biomass- and waste- fired boilers.

Corrosion

Waste

Chromate

Biomass

Chlorine

304L

KCl

Deposit

HC1, Hörsalsvägen 14, Chalmers Tekniska Högskola
Opponent: Prof. W. J. Quadakkers, Institute of Energy Research, Research Center Jülich, Germany

Författare

Jesper Liske

Chalmers, Kemi- och bioteknik, Oorganisk miljökemi

The influence of sulphur additions on the corrosive environment in a waste-fired CFB boiler

Materials Science Forum,; Vol. 522-523(2006)p. 563-570

Artikel i vetenskaplig tidskrift

Microstructural investigation of the influence of KCl on the corrosion of 304L exposed to 5% O2 + N2

16th International Corrosion Congress, September 19-24 2005, Beijing, China,; (2005)p. Paper 6-45

Paper i proceeding

Alkali Induced Corrosion of 304-type Austenitic Stainless Steel at 600°C; Comparison between KCl, K2CO3 and K2SO4

Materials Science Forum,; Vol. 595-598(2008)p. 367-375

Artikel i vetenskaplig tidskrift

KCl induced corrosion of a 304-type austenitic stainless steel at 600 degrees C; The role of potassium

Oxidation of Metals,; Vol. 64(2005)p. 23-41

Artikel i vetenskaplig tidskrift

A pilot plant study of the effect of alkali salts on initial stages of the high temperature corrosion of alloy 304L

Materials Science Forum,; Vol. 461-464(2004)p. 965-972

Artikel i vetenskaplig tidskrift

Ämneskategorier

Oorganisk kemi

Materialkemi

ISBN

978-91-7385-214-2

Doktorsavhandlingar vid Chalmers tekniska högskola. Ny serie: 2895

HC1, Hörsalsvägen 14, Chalmers Tekniska Högskola

Opponent: Prof. W. J. Quadakkers, Institute of Energy Research, Research Center Jülich, Germany