The Influence of Small Amounts of KCl(s) on the Initial Stages of the Corrosion of Alloy Sanicro 28 at 600 °C
Artikel i vetenskaplig tidskrift, 2008

The influence of KCl(s) on the oxidation of Sanicro 28 (35Fe27Cr31Ni) austenitic stainless steel at 600 °C in 5% O2 + 40% H2O and in 5% O2 was investigated. The samples were coated with 0.1 mg/cm2 KCl(s) prior to exposure. The exposure time was 1, 24, 72 and 168 h. Uncoated samples were exposed for reference. The oxidized samples were analyzed by SEM/energy-dispersive X-ray (EDX), X-ray diffraction (XRD), and AES. The amount of chloride and chromate on the samples was analyzed quantitatively by ion chromatography after exposure. KCl(s) is very corrosive towards Sanicro 28. Corrosion is initiated by the formation of potassium chromate through the reaction of KCl(s) with the protective oxide, chloride leaving the sample in the form of HCl. Chromate formation is a sink for chromium in the oxide and leads to a deterioration of its protective properties. In the 5% O2 + 40% H2O environment, there is a stoichiometric relationship between the chromate formed and the chloride consumed. In dry O2 chromate formation is relatively slow, leaving more unreacted KCl(s) on the surface than in 5% O2 + 40% H2O. Once the protective, chromium-rich oxide has been depleted in chromium by chromate formation, the alloy becomes susceptible to direct attack by the remaining KCl(s).

Sanicro 28

Oxidation

KCl

Chromate formation

Författare

Carolina Pettersson

Chalmers, Kemi- och bioteknik, Oorganisk miljökemi

Lars-Gunnar Johansson

Chalmers, Kemi- och bioteknik, Oorganisk miljökemi

Jan-Erik Svensson

Chalmers, Kemi- och bioteknik, Oorganisk miljökemi

Oxidation of Metals

0030-770X (ISSN) 1573-4889 (eISSN)

Vol. 70 5-6 241-256

Ämneskategorier

Oorganisk kemi

Materialkemi