Anisotropy of Room Temperature Ductility in Haynes 282 Forgings
Paper i proceeding, 2014

Haynes 282 is relatively new nickel base superalloy, offering excellent mechanical properties and attracting interest from the gas turbine and aerospace industry. One of the criteria for meeting specification requirement is the room temperature ductility.Forgings of Haynes 282 show large anisotropy in ductility, varying from approximately 25% in longitudinal transverse (LT) to 12% in the short transverse(ST) direction. In this paper LT and ST specimens from forgings were tested for its room temperature ductility.Fractographic and metallographic analysis show the presence of MC and Mc6C carbide banding. Failure in both ST and LT direction was ductile with intergranular fracture, but in the ST direction the failure was preferentially due to cracking of carbides. The orientation of carbides in preferred direction and their excessive segregation affecting ductility in ST is discussed in this work.

Tensile ductility

Microstructure

Haynes®282®

Författare

Ceena Joseph

Chalmers, Material- och tillverkningsteknik, Materialteknologi

Magnus Hörnqvist Colliander

Chalmers, Teknisk fysik, Materialens mikrostruktur

Christer Persson

Chalmers, Material- och tillverkningsteknik, Materialteknologi

Proceedings of the 8th International Symposium on Superalloy 718 and Derivatives

601-609
978-1-119-01680-9 (ISBN)

Ämneskategorier

Materialteknik

Annan materialteknik

Metallurgi och metalliska material

Styrkeområden

Materialvetenskap

DOI

10.1002/9781119016854.ch47

ISBN

978-1-119-01680-9

Mer information

Senast uppdaterat

2022-09-08