Pore-free bubbling delamination of chemical vapor deposited graphene from copper foils
Artikel i vetenskaplig tidskrift, 2015

The electrolytic bubbling-assisted transfer of graphene from metal catalysts in chemical vapor deposition provides a high efficiency, low cost and environmental benign alternative to the traditional chemical etching method. Despite its high potential, the yield of bubbling delamination is yet low, mainly due to the induced pores in the graphene after the transfer. It is found that water and protons transported through the poly(methyl methacrylate) (PMMA) supporting layer play a critical role in pore formation. Once water and protons reach the PMMA-graphene interface before delamination is finished, the protons permeate the graphene and form trapped hydrogen bubbles between the graphene and the metal. The built-up gas pressure inside the bubbles is high enough to crack the PMMA/graphene sheet, thereby creating pores in the graphene. An optimized PMMA layer not only reduces trapped hydrogen bubble generation, but it is also mechanically stronger preventing cracking. This contributes significantly to the pore-free electrolytic bubbling-assisted delamination of graphene.

Författare

Zhaoyao Zhan

Chalmers, Mikroteknologi och nanovetenskap, Kvantkomponentfysik

Jie Sun

Chalmers, Mikroteknologi och nanovetenskap, Kvantkomponentfysik

Lihui Liu

Chalmers, Mikroteknologi och nanovetenskap, Kvantkomponentfysik

Ergang Wang

Chalmers, Kemi och kemiteknik, Tillämpad kemi

Yu Cao

Chalmers, Material- och tillverkningsteknik, Yt- och mikrostrukturteknik

Niclas Lindvall

Chalmers, Mikroteknologi och nanovetenskap, Kvantkomponentfysik

Grigory Skoblin

Chalmers, Mikroteknologi och nanovetenskap, Kvantkomponentfysik

Avgust Yurgens

Chalmers, Mikroteknologi och nanovetenskap, Kvantkomponentfysik

Journal of Materials Chemistry C

20507526 (ISSN) 20507534 (eISSN)

Vol. 3 33 8634-8641

Styrkeområden

Nanovetenskap och nanoteknik

Ämneskategorier

Materialteknik

Nanoteknik

Infrastruktur

Nanotekniklaboratoriet

DOI

10.1039/c5tc01771h

Mer information

Senast uppdaterat

2023-08-08