Improvement in the Wear Resistance under Dry Friction of Electrodeposited Fe-W Coatings through Heat Treatments
Artikel i vetenskaplig tidskrift, 2019

The influence of the microstructural transformations upon heat treatments on the wear resistance of Fe-W coatings is studied. The coatings are electrodeposited from a glycolate-citrate plating bath with 24 at.% of W, and the wear resistance is investigated under dry friction conditions using ball-on-disc sliding tests. The samples were annealed in Ar atmosphere at different temperatures up to 800 °C. The microstructural transformations were studied by means of X-ray Diffraction (XRD), Scanning Electron Microscopy (SEM), and Electron Backscattered Diffraction (EBSD) technique. Except for the coating annealed at 800 °C, all the tested coatings suffered severe tribo-oxidation which resulted in the formation of deep cracks, i.e., ~15 μm in depth, within the wear track. The precipitation of the secondary phases, i.e., Fe2W and FeWO4, on the surface of the sample annealed at 800 °C increased the resistance to tribo-oxidation leading to wear tracks with an average depth of ~3 μm. Hence, the Fe-W coating annealed at 800 °C was characterized with a higher wear resistance resulting in a wear rate comparable to electrodeposited hard chromium coatings, i.e., 3 and 4 × 10−6 mm3/N m, respectively.

electrodeposition

wear resistance

iron-tungsten alloys

heat treatment

Författare

Antonio Mulone

Chalmers, Industri- och materialvetenskap, Material och tillverkning

Aliona Nicolenco

Vilniaus universitetas

Naroa Imaz

CIDETEC

Vanesa Martinez-Nogues

CIDETEC

Natalia Tsyntsaru

Vilniaus universitetas

Henrikas Cesiulis

Vilniaus universitetas

Uta Klement

Chalmers, Industri- och materialvetenskap, Material och tillverkning

Coatings

20796412 (eISSN)

Vol. 9 2 66-

Smart ELECTrodeposited Alloys for environmentally sustainable applications: from advanced protective coatings to micro/nano-robotic platforms (SELECTA)

Europeiska kommissionen (EU) (EC/H2020/642642), 2015-01-01 -- 2018-12-31.

Drivkrafter

Hållbar utveckling

Ämneskategorier

Tribologi

Metallurgi och metalliska material

Korrosionsteknik

Styrkeområden

Materialvetenskap

DOI

10.3390/coatings9020066

Mer information

Senast uppdaterat

2024-07-17