Three-dimensional bioprinting using a coaxial needle with viscous inks in bone tissue engineering - An in vitro study
Artikel i vetenskaplig tidskrift, 2020

Introduction: Vascularized autologous tissue grafts are considered 'gold standard' for the management of larger bony defects in the craniomaxillofacial area. This modality does however carry limitations, such as the absolute requirement for healthy donor tissues and recipient vessels. In addition, the significant morbidity of large bone graft is deterrent to fibula bone flap use. Therefore, less morbid strategies would be beneficial. The purpose of this study was to develop a printing method to manufacture scaffold structure with viable stem cells. Materials and Methods: In total, three different combinations of ground beta tri-calcium phosphate and CELLINK (bioinks) were printed with a nozzle to identify a suitable bioink for three-dimensional printing. Subsequently, a coaxial needle, with three different nozzle gauge combinations, was evaluated for printing of the bioinks. Scaffold structures (grids) were then printed alone and with additional adipose stem cells before being transferred into an active medium and incubated overnight. Following incubation, grid stability was evaluated by assessing the degree of maintained grid outline, and cell viability was determined using the live/dead cell assay. Results: Among the three evaluated combinations of bioinks, two resulted in good printability for bioprinting. Adequate printing was obtained with two out of the three nozzle gauge combinations tested. However, due to the smaller total opening, one combination revealed a better stability. Intact grids with maintained stability were obtained using Ink B23 and Ink B42, and approximately 80% of the printed stem cells were viable following 24 hours. Discussion: Using a coaxial needle enables printing of a stable scaffold with viable stem cells. Furthermore, cell viability is maintained after the bioprinting process.

viability

in vitro

CELLINK

Adipose stem cells

bioinks

Författare

Java Walladbegi

Göteborgs universitet

Christian Schaefer

Göteborgs universitet

Elin Pernevik

Chalmers, Kemi och kemiteknik, Tillämpad kemi

Sanna Sämfors

Chalmers, Kemi och kemiteknik, Tillämpad kemi

Göran Kjeller

Göteborgs universitet

Paul Gatenholm

Chalmers, Kemi och kemiteknik, Tillämpad kemi

George K. Sándor

Oulun Yliopisto

Lars Rasmusson

Göteborgs universitet

Universitetssjukhuset i Linköping

Annals of Maxillofacial Surgery

22310746 (ISSN) 22493816 (eISSN)

Vol. 10 2 370-376

Ämneskategorier

Biomaterialvetenskap

Medicinska material och protesteknik

Annan industriell bioteknik

DOI

10.4103/ams.ams_288_20

Mer information

Senast uppdaterat

2021-03-11