Role of HIPing and Heat Treatment on Properties of Alloy 718 Fabricated by Electron Beam Melting
Paper i proceeding, 2019

Although additive manufacturing (AM) of difficult-to-machine materials can open new design possibilities for production of parts with complex geometries, AM builds are characterized by presence of detrimental defects like shrinkage/ gas porosity and lack-of-fusion. Microstructural inhomogeneity, anisotropy in properties and formation of undesirable phases are added concerns. Motivated by the need for investigation of appropriate thermal post-treatments to eliminate defects, and to achieve desired microstructural and mechanical properties, the influence of hot isostatic pressing (HIPing) and heat treatment on electron beam melted (EBM) Alloy 718 specimens built at different heights from the base-plate has been studied. While HIPing led to orders of magnitude reduction in defect content, conventional heat treatment without applied pressure was found to have no effect. Thermal post-treatment was found to eliminate inherent variability in phase constitution and hardness of as-built specimens. HIPing at high temperature was accompanied by grain coarsening, suggesting modification of the HIPing protocol.

heat treatment


Hot isostatic pressing

Alloy 718

Electron beam melting

Additive Manufacturing


Sneha Goel

Högskolan Väst

Tejas Gundgire

Högskolan Väst

Johny Varghese

University of Hyderabad

Koteswararao V. V. Rajulapati

University of Hyderabad

Uta Klement

Chalmers, Industri- och materialvetenskap, Material och tillverkning

Shrikant Joshi

Högskolan Väst

Euro PM 2019 Congress and Exhibition

9781899072514 (ISBN)

Euro PM2019 – HIP Post Processing of AM Parts
Maastricht, Netherlands,


Bearbetnings-, yt- och fogningsteknik

Annan materialteknik

Metallurgi och metalliska material

Mer information

Senast uppdaterat