High-temperature creep resistant ternary blends based on polyethylene and polypropylene for thermoplastic power cable insulation

Artikel i vetenskaplig tidskrift, 2021

The impact of a small amount of polystyrene-b-poly(ethylene-co-butylene)-b-polystyrene (SEBS) on the thermomechanical and electrical properties of blends comprising low-density polyethylene (LDPE) and isotactic polypropylene (PP) is investigated. SEBS is found to assemble at the PP:LDPE interface as well as within isolated PP domains. The addition of 10 wt% SEBS significantly increases the storage modulus between the melting temperatures of the two polyolefins, 110 and 160°C, and results in improved resistance to creep during both tensile deformation as well as compression. Furthermore, the ternary blends display a very low direct-current (DC) conductivity as low as 3.4 × 10  S m at 70°C and 30 kV mm , which is considerably lower than values measured for neat LDPE. The here presented type of ternary blend shows potential as an insulation material for high-voltage direct current power cables.