Chemical vapor deposition of TiN on a CoCrFeNi multi-principal element alloy substrate
Artikel i vetenskaplig tidskrift, 2020

The reactivity of a quaternary multi-principal element alloy (MPEA), CoCrFeNi, as a substrate in thermal halide chemical vapor deposition (CVD) processes for titanium nitride (TiN) coatings was studied. The coatings were deposited at 850 °C–950 °C using TiCl4, H2 and N2 precursors. The coating microstructures were characterized using X-ray diffraction (XRD), scanning and transmission electron microscopy (SEM/TEM) with energy dispersive X-ray spectroscopy (EDS). Thermodynamic calculations of substrate and coating stability for a gas phase environment of N2 and H2 within a temperature range relevant for the experiments showed that Cr is expected to form hexagonal Cr2N and cubic (Ti1−ε1Crε1)N or (Cr1−ε2Tiε2)N phases. These phases could however not be discerned in the samples by XRD after the depositions. Cr was detected at the grain boundaries and the top surface by EDS for a sample synthesized at 950 °C. Grain boundary and surface diffusion, respectively, were the suggested mechanisms for Cr transport into the coating and onto the top surface. Although thermodynamic calculations indicated that Cr is the most easily etched component of the CoCrFeNi alloy to form gaseous chlorides in similar concentrations to that of the residual Ti-chlorides, no sign of etching were found according to the imaging of the sample cross-sections using SEM and TEM. Cross-section and top surface images further confirmed that the choice of substrate had no significant detrimental influence on the film growth or microstructure.


multi-principle element alloy

transmission electron microscopy

X-ray diffraction

Titanium nitride

chemical vapour deposition


Katalin Böör

Uppsala universitet

Ren Qiu

Chalmers, Fysik, Mikrostrukturfysik

Axel Forslund

Kungliga Tekniska Högskolan (KTH)

Olof Bäcke

Chalmers, Fysik, Mikrostrukturfysik

Henrik Larsson

Kungliga Tekniska Högskolan (KTH)

Erik Lindahl


Mats Halvarsson

Chalmers, Fysik, Mikrostrukturfysik

Mats Boman

Uppsala universitet

L. von Fieandt


Surface and Coatings Technology

0257-8972 (ISSN)

Vol. 393 125778

CVD 2.0 - En ny generation av hårda beläggningar

Stiftelsen för Strategisk forskning (SSF) (RMA15-0048), 2016-05-01 -- 2021-06-30.


Oorganisk kemi

Metallurgi och metalliska material

Annan elektroteknik och elektronik





Grundläggande vetenskaper


Innovation och entreprenörskap


Chalmers materialanalyslaboratorium

Lärande och undervisning

Pedagogiskt arbete



Mer information

Senast uppdaterat