Dispersive Effects in Microwave AlGaN/AlN/GaN HEMTs With Carbon-Doped Buffer

Journal article, 2015

Aluminium gallium nitride (AlGaN)/GaN high-electron mobility transistor performance is to a large extent affected by the buffer design, which, in this paper, is varied using different levels of carbon incorporation. Three epitaxial structures have been fabricated: 1) two with uniform carbon doping profile but different carbon concentration and 2) one with a stepped doping profile. The epitaxial structures have been grown on 4H-SiC using hot-wall metal-organic chemical vapor deposition with residual carbon doping. The leakage currents in OFF-state at 10 V drain voltage were in the same order of magnitude (10(-4) A/mm) for the high-doped and stepped-doped buffer. The high-doped material had a current collapse (CC) of 78.8% compared with 16.1% for the stepped-doped material under dynamic I-V conditions. The low-doped material had low CC (5.2%) but poor buffer isolation. Trap characterization revealed that the high-doped material had two trap levels at 0.15 and 0.59 eV, and the low-doped material had one trap level at 0.59 eV.