Oxide Transformation During Sintering Of Prealloyed Water Atomized Steel Powder
Paper i proceeding, 2010

Some amount of oxides are already present on the initial powder surface and its interior, however further oxide products formation and their transformation during sintering remains unclear. The present study deals with the modelling of oxides transformation in dependence on sintering atmosphere composition, its purity and temperature profile utilizing variety of chemical and thermodynamic softwares based on experimental results from interrupted sintering trials. As the base material prealloyed with chromium water atomized steel powder was used. The type, morphology and composition of oxide products on the fracture surface were studied by means of HR SEM combined with EDX analysis. Results indicate that oxide transformation processes occur in accordance with the thermodynamic stability of oxides, presented on the initial powder surface, in the line Fe2O3→FeO→Fe2MnO4→Cr2FeO4→Cr2O3→MnCr2O4→MnO. Amount and composition of surface products are strongly determined not only by conditions during dwelling at sintering temperature but also by processes during preceding heating stage.

surface oxide

sintering atmosphere

oxide reduction

surface analysis

Alloyed sintered steels

Författare

Eduard Hryha

Chalmers, Material- och tillverkningsteknik, Yt- och mikrostrukturteknik

Lars Nyborg

Chalmers, Material- och tillverkningsteknik, Yt- och mikrostrukturteknik

World Powder Metallurgy Congress and Exhibition, World PM 2010; Florence; Italy; 10 October 2010 through 14 October 2010

Vol. 2 268-275

Ämneskategorier

Bearbetnings-, yt- och fogningsteknik

Annan materialteknik

ISBN

978-189907219-4

Mer information

Skapat

2017-10-07