Effects of BN and SiC nanoparticles on properties of conductive adhesive
Paper i proceeding, 2010

Isotropic conductive adhesives (ICAs) are a type of interconnect material used more and more widely in computer, robot, mobile phone, LED and so on. Compared with traditional solders, isotropic conductive adhesives have better working plasticity, creep resistance and heat resistance. In particular, isotropic conductive adhesives are more responsive in high density packaging than solder, which determines the dominance of ICAs in high density packaging in the future. In order to improve the thermal conductivity of ICA with acceptable electrical conductivity, Ag flakers, BN and SiC nanoparticles were added into the matrix. The content of silver flakes was 75wt%, and the content of nanoparticles (BN or SiC) in the isotropic conductive adhesives were 0wt%, 0.5wt%, 1.5wt%, 2.5wt%, 3wt%, 5wt% in weight. The conductive adhesives were coated on the PCBs with stencil printing and fifty SR1206 chip components were mounted on a PCB using conductive adhesive. All samples were cured at 150°for 1h. Further research into the reliability of the above isotropic conductive adhesives after temperature & humidity and thermal-cycling was carried out to analyze the effects of BN and SiC nanoparticals on the properties of ICA. The condition of the temperature & humidity test was 85 ° /85%RH, 500h. The thermal-cycling test was -40 °∼125°, 500 cycles and the soaking time and ramping rate were 19min and ±15°/min. Changes to electrical resistance were used to estimate the reliability of the isotropic conductive adhesives in this study. The microstructure of the failure samples was observed using a Scanning Electron Microscope (SEM). The water absorption of all ICAs is the same after 94h temperature and humidity aging and the rate of water absorption is also the same during the aging. The ICA with 3% boron nitride nanoparticles and 75% micron silver flakes shows the best temperature and humidity reliability, with the fewest cracks on the interface between ICA and component. After 500h thermal cycling aging, the resistance reduces in the first 100h and maintains in a certain value after 332h cycled thermal. The samples have no wide cracks but a few small ones on the interface. © 2010 IEEE.

Författare

Huaxiang Lai

Shanghai University

Xiuzhen Lu

Shanghai University

H. Cui

Shanghai University

SMIT Ltd. Co.

X. Liu

SMIT Ltd. Co.

Si Chen

SMIT Ltd. Co.

Shanghai University

T. Chen

Shanghai University

Johan Liu

Chalmers, Teknisk fysik, Elektronikmaterial

Proceedings - 2010 11th International Conference on Electronic Packaging Technology and High Density Packaging, ICEPT-HDP 2010; Xi'an; 16 August 2010 through 19 August 2010

Article number 5582434 235-239
978-142448142-2 (ISBN)

Ämneskategorier

Fysik

DOI

10.1109/ICEPT.2010.5582434

ISBN

978-142448142-2

Mer information

Skapat

2017-10-08