Lean atmospheres for sintering chromium alloyed PM steels
Paper i proceeding, 2013

Hydrogen and carbon monoxide are effective reducing agents at different temperature ranges and there is only scarce experimental and theoretical data about their interaction and combined reducing effect at dry conditions and low amount. The work presents experimental and theoretical evaluation of the reducing and carburizing activity of lean nitrogen-based atmospheres containing hydrogen, carbon monoxide and small additions of hydrocarbons with their total content in the range of 0.3 to 5 vol%. Effect of carbon content (0 and 0.4 wt%) and temperature profile in the case of sintering of chromium prealloyed PM steels was evaluated. Results indicate that the carbon pickup increases with increasing CO content in the atmosphere, however it brings significant risk of oxidation. Atmospheres with low content of CO and H2 (<1.5 vol% of both) and small hydrocarbon additions showed to be good candidates for robust sintering of chromium alloyed PM steels.

lean sintering atmosphere

oxide reduction

carburizing

endogas type atmospheres

Författare

Seshendra Karamchedu

Chalmers, Material- och tillverkningsteknik, Yt- och mikrostrukturteknik

Eduard Hryha

Chalmers, Material- och tillverkningsteknik, Yt- och mikrostrukturteknik

Sigurd Berg

Sören Wiberg

Lars Nyborg

Chalmers, Material- och tillverkningsteknik, Yt- och mikrostrukturteknik

Proceedings of Euro PM2013

Vol. 2 353-358

Drivkrafter

Hållbar utveckling

Styrkeområden

Produktion

Ämneskategorier

Metallurgi och metalliska material

Mer information

Skapat

2017-10-07