Disc brakes for heavy vehicles: An experimental study of temperatures and cracks
Artikel i vetenskaplig tidskrift, 2015

A better understanding of the thermomechanical loading of brake discs is important for controlling material fatigue and crack propagation in the disc. In the present study, full-scale drag braking experiments were performed on brake discs made from eight different grey cast iron alloys. The well-performing materials were also tested with an alternative brake pad material. A testing procedure with repeated drag brakings was used. The disc and pad temperatures were registered by thermocouples embedded at selected locations, and the disc surface temperatures by a thermocamera. Extensive analyses of the measured temperatures were performed. The results for the thermocouples at the mid-radius of the disc and at the end of brake applications indicatd that the two sides of the disc have opposite deviations from the mean temperature. The temperature deviations are generally temporally alternating, but also stationary variations can be found. The thermocamera gives the possibility of identifying the phenomena behind the temperature variations found from the thermocouples. Banding of the disc–pads contact with alternating one band and two bands of high temperatures is observed for the studied brake discs exposed to severe braking load cases. Moreover, it was found that hot-spot patterns develop on the disc surface, which are spatially fixed during each brake application. However, they may be either slowly migrating or fixed relative to the disc during consecutive brake applications. Thermal images show that small cracks do not affect hot-spot migration as a hot spot migrates over the crack. However, at a critical length of the crack, the heat becomes localized at the crack and increases its growth, thus limiting the life of the disc. The tests indicate that a combination of hot-spot migration, alternating bands and small temperature differences over the disc are significant factors to be considered when improving the lifespan of the discs.

drag braking

hot spots

disc braking

laboratory experiments

disc

temperature

grey iron

cracks

Författare

Gael le Gigan

Dynamik

Tore V Vernersson

Dynamik

Roger Lundén

Dynamik

Peter Skoglund

Scania CV AB

Proceedings of the Institution of Mechanical Engineers, Part D: Journal of Automobile Engineering

0954-4070 (ISSN) 2041-2991 (eISSN)

Vol. 229 6 684-707

Styrkeområden

Transport

Materialvetenskap

Ämneskategorier

Teknisk mekanik

Farkostteknik

DOI

10.1177/0954407014550843

Mer information

Senast uppdaterat

2019-11-29