Effect of thermal cycling on protective properties of alumina scale grown on thin Haynes 214 foil
Artikel i vetenskaplig tidskrift, 2015

The isothermal and cyclic oxidation of a thin alloy 214 foil (130μm thick) has been studied in air at 1200°C for up to 720 h. Haynes 214 forms a duplex oxide scale consisting of pure, columnar alumina overlaid by mixed Ni(Al,Cr) 2 O 4 spinel with minor inclusions of (Al,Cr) 2 O 3 . A transition from external alumina to chromia scaling (abbreviated as TACS) occurs at the oxide-alloy interface after the Al reservoir of the foil is exhausted due to oxidation. The tensile cracking of the oxide scale upon thermal cycling is shown to promote the early transition from protective to accelerated breakaway oxidation. © 2015 Elsevier Ltd.

A. Nickel

B. Thermal cycling


C. Oxidation

C. High temperature corrosion

A. Alloy


A. Chyrkin

Forschungszentrum Jülich

Nooshin Mortazavi Seyedeh

Chalmers, Teknisk fysik, Materialens mikrostruktur

Mats Halvarsson

Chalmers, Teknisk fysik, Materialens mikrostruktur

D. Grüner

Forschungszentrum Jülich

W. J. Quadakkers

Forschungszentrum Jülich

Corrosion Science

0010-938X (ISSN)

Vol. 98 688-698


Bearbetnings-, yt- och fogningsteknik



Mer information

Senast uppdaterat