The Role of Carbon Source in the Production of Ultrafine and Nanocrystalline WC-6Co Cemented Carbides
Paper i proceeding, 2015

Tungsten carbide powders are typically produced either by carburization of tungsten metal powders (W) or by carbothermal reduction of tungsten oxide powders (WO3). Different powders can be used as carburizing source like carbon black and graphite. Synthesis of nanostructured WC powders is achieved by a two-step process: mechanical activation of initial powders (by milling), followed by thermal activation of mixes. The properties and microstructure of the resulting tungsten carbide powders (WC) can be influenced both by the raw materials and by the mixing / carburization conditions (temperature and atmosphere). This work presents the effect of the carbon source reactivity (synthetic graphite and different carbon black types) on the synthesis of nanocrystalline WC powders and ultrafine WC-6Co cemented carbides. This experimental work sets the basis for optimizing the production of nano-WC powders based on raw material selection and process conditions.

Nanocrystalline WC-powders

ultrafine cemented carbides

reactivity

graphite

carbon black

Författare

Raffaele Gilardi

Imerys

Luigi Alzati

Imerys

Raquel Oro

Technische Universität Wien

Eduard Hryha

Chalmers, Material- och tillverkningsteknik, Yt- och mikrostrukturteknik

Lars Nyborg

Chalmers, Material- och tillverkningsteknik, Yt- och mikrostrukturteknik

Sigurd Berg

Hoganas

L Radicchi

Sigmacarb SA

roceedings EURO PM2015 Congress & Exhibition, 4-7 October 2015, Reims, France

1-6

Drivkrafter

Hållbar utveckling

Styrkeområden

Produktion

Materialvetenskap

Ämneskategorier

Annan materialteknik

Metallurgi och metalliska material

ISBN

978-1-899072-47-7