Permeability of water and oleic acid in composite films of phase separated polypropylene and cellulose stearate blends
Artikel i vetenskaplig tidskrift, 2016
Cellulose esters with long carbon side chains (e.g. stearate) were produced via a homogenous reaction in ionic liquids. The degree of substitution was calculated to approximately 2. The melt rheology was studied for the pure cellulose esters but also combinations of the esters and polypropylene to study the processability of a blended composite material. It was shown that the compatibility between the two components was weak, which resulted in a phase-separated composite material. The morphology and permeability of water and oleic acid of the composite films were studied and it was shown that the water permeability decreased upon addition of the cellulose ester to the polymer. The permeability of oleic acid was however unchanged, which is most probable a result of high solubility in the cellulose ester rich domains of the composites. Also, the following hypothesis is stated: cellulose stearate influence the polypropylene crystallization process by decreasing the size of spherulites. (C) 2016 Elsevier Ltd. All rights reserved.
nanocomposites
ionic liquids
dispersion
Cellulose stearate
Polypropylene
Spherulites
Permeability
esters
acylation
Polymer Science
1-butyl-3-methylimidazolium chloride
Chemistry
polyethylene
Polymer blending
derivatives
Författare
I. Krasnou
Tallinns tekniska universitet (TalTech)
Sofie Gårdebjer
Chalmers, Kemi och kemiteknik, Tillämpad kemi
E. Tarasova
Tallinns tekniska universitet (TalTech)
Anette Larsson
Chalmers, Kemi och kemiteknik, Tillämpad kemi
Gunnar Westman
Chalmers, Kemi och kemiteknik, Kemi och biokemi
A. Krumme
Tallinns tekniska universitet (TalTech)
Carbohydrate Polymers
0144-8617 (ISSN) 18791344 (eISSN)
Vol. 152 450-458Ämneskategorier (SSIF 2011)
Polymerkemi
Organisk kemi
Styrkeområden
Produktion
Materialvetenskap
DOI
10.1016/j.carbpol.2016.07.016
PubMed
27516292