Study of flank wear topography and surface-deformation of cemented carbide tools after turning Alloy 718
Paper i proceeding, 2018

An investigation is reported on the characterization of an uncoated tungsten carbide tool used for machining of a Ni-Fe based superalloy (Alloy 718). Scanning electron microscopy (SEM) in combination with white-light interferometry (WLI) was applied to study the flank wear surface topographies both directly after the turning test and when the adhered workpiece material was removed by etching. The obtained results show that the thin layers of adhered workpiece material present on the flank wear land can obscure the wear topography. Removal of adhered workpiece material from the worn areas of interest is therefore necessary to reveal features of worn tool surfaces. SEM observations of worn WC grains revealed that abrasion is an active wear mechanism during cutting. Complementary analysis by the electron backscatter diffraction (EBSD) technique revealed that worn WC grains are additionally characterized by significant strain which suggests the contribution of plastic deformation to the flank wear. Plastic deformation of WC is likely caused by high thermal and mechanical loads acting on the tool during machining.

Scanning electron microscopy

Tool wear

Electron backscatter diffraction

Turning

Tribology

Författare

Philipp Hoier

Chalmers, Industri- och materialvetenskap, Material och tillverkning

Amir Malakizadi

Chalmers, Industri- och materialvetenskap, Material och tillverkning

Peter Krajnik

Chalmers, Industri- och materialvetenskap, Material och tillverkning

Uta Klement

Chalmers, Industri- och materialvetenskap, Material och tillverkning

Procedia CIRP

22128271 (eISSN)

Vol. 77 537-540

8th CIRP Conference on High Performance Cutting, HPC 2018
Budapest, Hungary,

Ämneskategorier

Tribologi

Bearbetnings-, yt- och fogningsteknik

Styrkeområden

Produktion

DOI

10.1016/j.procir.2018.08.239

Mer information

Senast uppdaterat

2023-03-21