Artikel i vetenskaplig tidskrift, 2021

Polar polythiophenes with oligoethylene glycol side chains are exceedingly soft materials. A low glass transition temperature and low degree of crystallinity prevents their use as a bulk material. The synthesis of a copolymer comprising 1) soft polythiophene blocks with tetraethylene glycol side chains, and 2) hard urethane segments is reported. The molecular design is contrary to that of other semiconductor-insulator copolymers, which typically combine a soft nonconjugated spacer with hard conjugated segments. Copolymerization of polar polythiophenes and urethane segments results in a ductile material that can be used as a free-standing solid. The copolymer displays a storage modulus of 25 MPa at room temperature, elongation at break of 95%, and a reduced degree of swelling due to hydrogen bonding. Both chemical doping and electrochemical oxidation reveal that the introduction of urethane segments does not unduly reduce the hole charge-carrier mobility and ability to take up charge. Further, stable operation is observed when the copolymer is used as the active layer of organic electrochemical transistors.

polar conjugated polymers

chemical and electrochemical doping

swelling

urethane

organic electrochemical transistors (OECT)

Författare

Sepideh Zokaei

Chalmers, Kemi och kemiteknik, Tillämpad kemi, Christian Müller Group

Renee Kroon

Chalmers, Kemi och kemiteknik, Tillämpad kemi, Christian Müller Group

Johannes Gladisch

Linköpings universitet

Wallenberg Wood Science Center (WWSC)

Bryan D. Paulsen

Northwestern University

Wonil Sohn

Northwestern University

Anna Hofmann

Chalmers, Kemi och kemiteknik, Tillämpad kemi, Christian Müller Group

Gustav Persson

Chalmers, Fysik, Nano- och biofysik

Arne Stamm

Kungliga Tekniska Högskolan (KTH)

Per Olof Syrén

Kungliga Tekniska Högskolan (KTH)

Wallenberg Wood Science Center (WWSC)

Eva Olsson

Chalmers, Fysik, Nano- och biofysik

Jonathan Rivnay

Northwestern University

Eleni Stavrinidou

Linköpings universitet

Wallenberg Wood Science Center (WWSC)

Anja Lund

Chalmers, Kemi och kemiteknik, Tillämpad kemi

Christian Müller

Chalmers, Kemi och kemiteknik, Tillämpad kemi, Christian Müller Group

Wallenberg Wood Science Center (WWSC)

Advanced Science

2198-3844 (ISSN)

Vol. 8 2 2002778

Ämneskategorier

Polymerkemi

Oorganisk kemi

Materialkemi

DOI

10.1002/advs.202002778

Mer information

Senast uppdaterat

2021-02-12