Exploring the Effect of Silicon on the High Temperature Corrosion of Lean FeCrAl Alloys in Humid Air
Artikel i vetenskaplig tidskrift, 2021

A new approach to reduce the chromium and aluminium concentrations in FeCrAl alloys without significantly impairing corrosion resistance is to alloy with 1-2 wt.% silicon. This paper investigates the "silicon effect" on oxidation by comparing the oxidation behavior and scale microstructure of two FeCrAl alloys, one alloyed with silicon and the other not, in dry and wet air at 600 degrees C and 800 degrees C. Both alloys formed thin protective oxide scales and the Cr-evaporation rates were small. In wet air at 800 degrees C the Si-alloyed FeCrAl formed an oxide scale containing mullite and tridymite together with alpha- and gamma-alumina. It is suggested that the reported improvement of the corrosion resistance of Al- and Cr-lean FeCrAl's by silicon alloying is caused by the appearance of Si-rich phases in the scale.

FeCrAl Alloy

Cr-evaporation

Oxidation

Mullite

Silicon

Författare

Tommy Sand

Chalmers, Kemi och kemiteknik, Energi och material, Oorganisk miljökemi

Aina Edgren

Chalmers, Kemi och kemiteknik, Energi och material, Oorganisk miljökemi

Christine Geers

Chalmers, Kemi och kemiteknik, Energi och material, Oorganisk miljökemi

Vijayshankar Asokan

Chalmers, Kemi och kemiteknik, Energi och material, Oorganisk miljökemi

Johan Eklund

Chalmers, Kemi och kemiteknik, Energi och material, Oorganisk miljökemi

T. Helander

Kanthal AB

Jan-Erik Svensson

Chalmers, Kemi och kemiteknik, Energi och material, Oorganisk miljökemi

Lars-Gunnar Johansson

Chalmers, Kemi och kemiteknik, Energi och material, Oorganisk miljökemi

Oxidation of Metals

0030-770X (ISSN) 1573-4889 (eISSN)

Vol. In Press

Ämneskategorier

Annan materialteknik

Metallurgi och metalliska material

Korrosionsteknik

DOI

10.1007/s11085-020-10019-2

Mer information

Senast uppdaterat

2021-02-18