Efficacy of an external chromia layer in reducing nitridation of high temperature alloys
Artikel i vetenskaplig tidskrift, 2022

Six high temperature alloys have been exposed in N2/H2 environments at 900 °C. In order to study the efficacy of a chromia barrier layer against nitrogen ingress, experiments were performed in two environments having the same N2/H2 ratio but slightly different water content, chromia formation being spontaneous in one case only. The samples were evaluated by SEM/STEM/EDX, XRD, gravimetry and GD-OES. The presence of an external chromia scale reduced nitridation of the alloy by 50–95%. Furthermore, in the presence of a continuous alumina layer no nitridation of the alloy was detected.

B. XRD

B. SEM

C. Oxidation

A. Alloy

B. STEM

C. High temperature corrosion

Författare

Tommy Sand

Chalmers, Kemi och kemiteknik, Energi och material, Oorganisk miljökemi 1

S. Bigdeli

Swerim AB

Mohammad Sattari

Chalmers, Fysik, Mikrostrukturfysik

J. Andersson

Sandvik

M. Hattestrand

Sandvik

T. Helander

Kanthal AB

Johan Eklund

Chalmers, Kemi och kemiteknik, Energi och material, Oorganisk miljökemi 1

Jan-Erik Svensson

Chalmers, Kemi och kemiteknik, Energi och material, Oorganisk miljökemi 1

Mats Halvarsson

Chalmers, Fysik, Mikrostrukturfysik

Lars-Gunnar Johansson

Chalmers, Kemi och kemiteknik, Energi och material, Oorganisk miljökemi 1

Corrosion Science

0010-938X (ISSN)

Vol. 197 110050

Ämneskategorier

Annan materialteknik

Metallurgi och metalliska material

Korrosionsteknik

DOI

10.1016/j.corsci.2021.110050

Mer information

Senast uppdaterat

2022-01-17