A Comparison of the Oxidation and Nitridation Properties of Selected Chromia- and Alumina-Forming Alloys at 800 degrees C

Artikel i vetenskaplig tidskrift, 2022

Three FeCrAl alloys and two chromia-formers (a stainless steel, and a Ni-base alloy) have been exposed in four environments (dry air, air + 20% H2O, 20% H-2 + 20% H2O + Ar and 95% N-2 + 5% H-2) for 168 h at 800 degrees C. The corroded samples were investigated by SEM/EDS, XRD and gravimetry, and the formation of CrO2(OH)(2)(g) was measured as a function of time using a denuder technique. The Fe-base alloy formed a Cr-rich protective oxide scale in dry air and wet air but suffered break-away oxidation in 20% H-2 + 20% H2O + Ar. In contrast, the Ni-base alloy suffered extensive NiO formation and internal oxidation in dry air and wet air but formed a protective chromia scale in 20% H-2 + 20% H2O. All three FeCrAl alloys formed protective alumina scales in dry air, wet air and 20% H-2 + 20% H2O + Ar. The FeCrAl alloy Kanthal APMT was severely nitrided in the 95% N-2 + 5% H-2 environment due to defects in the oxide scale associated with RE-rich inclusions which allowed nitrogen to enter the alloy. In contrast, the two Cr-lean FeCrAl alloys Kanthal EF101 and Kanthal EF100 did not suffer nitridation at all.