A hexagon based Mn(ii) rod metal-organic framework - structure, SF6 gas sorption, magnetism and electrochemistry
Artikel i vetenskaplig tidskrift, 2023

A manganese(ii) metal-organic framework based on the hexatopic hexakis(4-carboxyphenyl)benzene, cpb6−: [Mn3(cpb)(dmf)3], was solvothermally prepared showing a Langmuir area of 438 m2 g−1, rapid uptake of sulfur hexafluoride (SF6) as well as electrochemical and magnetic properties, while single crystal diffraction reveals an unusual rod-MOF topology.

Författare

Francoise Mystere Amombo Noa

Chalmers, Kemi och kemiteknik, Kemi och biokemi

O. Cheung

Uppsala universitet

Michelle Åhlén

Uppsala universitet

Elisabet Ahlberg

Göteborgs universitet

Priyanka Nehla

Uppsala universitet

Germán Salazar-Alvarez

Uppsala universitet

Soheil Ershadrad

Uppsala universitet

Biplab Sanyal

Uppsala universitet

Lars Öhrström

Chalmers, Kemi och kemiteknik, Kemi och biokemi

Chemical Communications

1359-7345 (ISSN) 1364-548X (eISSN)

Vol. 59 15 2106-2109

Ämneskategorier

Oorganisk kemi

Materialkemi

Annan kemi

DOI

10.1039/d2cc06916d

PubMed

36723213

Mer information

Senast uppdaterat

2024-03-07