Intergranular oxidation of additively manufactured Ni-base alloy 625: The role of Si
Artikel i vetenskaplig tidskrift, 2023

Additively manufactured (AM) Ni-base alloy 625 exposed in air and H2/H2O at 900 °C has been shown to suffer from intergranular oxidation attack unlike its conventionally manufactured (CM) variant. Modification of the AM microstructure via hot-rolling and heat-treatment did not alter the oxidation pattern. Detailed analysis of minor differences in chemical composition of AM and CM exposed the critical role of Si in oxidation protection of alloy 625. Experiments with model alloys as well as diffusion modeling confirmed the crucial role of a minimum Si concentration to form a SiO2 subscale preventing thereby intergranular oxidation attack.

High-temperature corrosion

Alloy 625

Intergranular oxidation

Additive manufacturing

Oxidation

Ni-base alloys

Författare

Anton Chyrkin

Chalmers, Kemi och kemiteknik, Energi och material

W. J. Nowak

Politechnika Rzeszowska

Kerem Gündüz

Gebze Teknik Üniversitesi (GYTE)

Chalmers, Kemi och kemiteknik, Energi och material

Irina Fedorova

Chalmers, Fysik, Mikrostrukturfysik

Mohammad Sattari

Chalmers, Fysik, Mikrostrukturfysik

Jan Froitzheim

Chalmers, Kemi och kemiteknik, Energi och material

Mats Halvarsson

Chalmers, Fysik, Mikrostrukturfysik

Marta Krystyna Stiller

Chalmers, Fysik, Mikrostrukturfysik

Corrosion Science

0010-938X (ISSN)

Vol. 219 111234

Undersökning av kolinducerad korrosion under dubbel atmosfär

Stiftelsen för Strategisk forskning (SSF) (UKR22-0047), 2022-07-01 -- 2024-12-31.

Ämneskategorier

Bearbetnings-, yt- och fogningsteknik

Metallurgi och metalliska material

DOI

10.1016/j.corsci.2023.111234

Mer information

Senast uppdaterat

2023-05-25