Dynamic recrystallization during hot compression of Ni-based superalloy Haynes 282
Artikel i vetenskaplig tidskrift, 2023

Understanding the microstructural behaviour of materials during thermomechanical processing is a vital step towards optimizing the mechanical properties. One important aspect during forming processes, such as forging, is dynamic recrystallization (DRX), which sets the starting microstructure for the subsequent manufacturing steps. Here we investigated the DRX behaviour of Ni-base superalloy Haynes 282 during hot compression with a strain rate of 0.05 s−1 at 1080 °C, with care taken to minimize the effects of meta-dynamic recrystallization (mDRX) and adiabatic heating. Small DRX grains could be observed already at ε = 0.1, i.e. before the peak strain εp = 0.15. The DRX process accelerated significantly above ε = 0.2, and the material was fully recrystallized at ε = 1.5. Up to ε = 0.8 DRX occurred through continuous nucleation of new grains, whereas above ε = 0.8 the number density of DRX grains decreased and the increase in recrystallized fraction was due to growth of existing grains. Contrary to common assumptions of DRX nuclei being essentially dislocation free, many of the DRX grains contained pronounced dislocation substructures, even at small strains where they are not expected to have undergone deformation.

Ni-base superalloys

EBSD

Dynamic recrystallization

Hot deformation

Författare

Emil Eriksson

Chalmers, Fysik, Mikrostrukturfysik

Fabian Hanning

Högskolan Väst

Joel Håkan Andersson

Högskolan Väst

Magnus Hörnqvist Colliander

Chalmers, Fysik, Mikrostrukturfysik

Journal of Alloys and Compounds

0925-8388 (ISSN)

Vol. 960 170837

Ämneskategorier

Bearbetnings-, yt- och fogningsteknik

Annan materialteknik

Metallurgi och metalliska material

Infrastruktur

Chalmers materialanalyslaboratorium

Styrkeområden

Materialvetenskap

DOI

10.1016/j.jallcom.2023.170837

Mer information

Senast uppdaterat

2023-07-04