Rheological and Functional Properties of Mechanically Recycled Post-Consumer Rigid Polyethylene Packaging Waste
Artikel i vetenskaplig tidskrift, 2024

The properties of recycled post-consumer rigid polyethylene packaging waste were studied, using sorted waste washed in the laboratory with water alone and with added detergent, and compared with large-scale high-intensity washed flakes. The washed flakes were compounded using three different temperature profiles in a twin-screw extruder and then injection molded. A higher compounding temperature reduced the thermo-oxidative stability, the average molecular mass, and the viscosity of the samples. Rheological measurements suggested that changes in chain branching occurred at different compounding temperatures. The strength and the elongation at break were also influenced by the compounding temperature in both the molten and solid states. Detergent washing maintained the thermo-oxidative stability in contrast to washing with water. The large-scale washed samples had a relatively high thermo-oxidative stability, a higher melt elasticity, and a lower elongation at break in both the molten and solid states than the laboratory-scale washed samples. The thermal properties, melt elasticity, Young’s modulus, yield stress, and yield strain of the samples were not, however, significantly affected by either the compounding temperature or the washing medium and intensity. The results indicated that recycled post-consumer rigid polyethylene packaging waste has properties that can support further applications in new products.

polyethylene

washing

rigid plastic packaging waste

mechanical properties

melt strength

plastic recycling

rheological properties

Författare

Ezgi Ceren Boz Noyan

Chalmers, Industri- och materialvetenskap, Konstruktionsmaterial

Franziska Rehle

Université de Montréal

Antal Boldizar

Chalmers, Industri- och materialvetenskap, Konstruktionsmaterial

Materials

19961944 (eISSN)

Vol. 17 8 1855

Återvinning av insamlad plast från förpackningar

Plastkretsen (PK) AB:s Stiftelse för forskning (-), 2020-06-01 -- 2024-12-31.

Drivkrafter

Hållbar utveckling

Ämneskategorier

Materialteknik

Polymerteknologi

Annan materialteknik

Fundament

Grundläggande vetenskaper

Styrkeområden

Materialvetenskap

DOI

10.3390/ma17081855

Mer information

Senast uppdaterat

2024-05-08