The effect of temperature on chromium vaporization and oxide scale growth on interconnect steels for Solid Oxide Fuel Cells
Artikel i vetenskaplig tidskrift, 2015

Chromium vaporization and oxide scale growth are probably the two most important degradation mechanisms associated with the interconnect in Solid Oxide Fuel Cells (SOFCs) when Cr 2 O 3 -forming alloys are used as the interconnect material. This study examines the influence of temperature on both mechanisms. Two commercially available steels; Crofer 22 H and Sanergy HT, were isothermally exposed at 650, 750 and 850 °C in an air-3% H 2 O atmosphere with a high flow rate. Volatile chromium species were collected using the denuder technique. The microstructure of thermally grown oxide scales was characterized using Scanning Electron Microscopy (SEM), Energy Dispersive X-Ray Analysis (EDX) and X-Ray Diffraction (XRD). The findings of this study show that although Cr evaporation is reduced with lower temperature, its relative importance compared to oxide scale growth is greater.

Sanergy

Interconnect

Cr vaporization

SOFC

Crofer

Oxidation

Författare

Hannes Falk Windisch

Chalmers, Kemi och kemiteknik, Energi och material

Jan-Erik Svensson

Chalmers, Kemi och kemiteknik, Energi och material

Jan Froitzheim

Chalmers, Kemi och kemiteknik, Energi och material

Journal of Power Sources

0378-7753 (ISSN)

Vol. 287 25-35

Ämneskategorier

Metallurgi och metalliska material

DOI

10.1016/j.jpowsour.2015.04.040

Mer information

Skapat

2017-10-07