Influence of pre-oxidation on dual atmosphere effect on AISI 441 interconnects for solid oxide fuel cell applications
Paper i proceeding, 2017

In previous studies an extreme dual atmosphere effect on the airfacing side of AISI 441 at 600°C was observed. However indications showed that pre-oxidation of the material might have a beneficial effect on the corrosion resistance in dual atmosphere. To examine this further we pre-oxidized AISI 441 samples for 0 min, 11 min, 45 min, 180 min and 280 min and subsequently exposed these at 600 °C for 500 h under dual atmosphere conditions. Photographs of the air-facing sides were taken throughout exposure to monitor the corrosion behavior. SEM analysis was performed on all samples after exposure.

Författare

Claudia Goebel

Chalmers, Kemi och kemiteknik, Energi och material

Patrik Alnegren

Chalmers, Kemi och kemiteknik, Energi och material

Robin Faust

Chalmers, Kemi och kemiteknik, Energi och material

Jan-Erik Svensson

Chalmers, Kemi och kemiteknik, Energi och material

Jan Froitzheim

Chalmers, Kemi och kemiteknik, Energi och material

ECS Transactions

19386737 (ISSN) 19385862 (eISSN)

Vol. 78 1 1559-1563

Infrastruktur

Chalmers materialanalyslaboratorium

Ämneskategorier

Korrosionsteknik

DOI

10.1149/07801.1559ecst

Mer information

Senast uppdaterat

2022-08-10