The efficiency of HFMI treatment and TIG remelting for extending the fatigue life of existing welded structures
Artikel i vetenskaplig tidskrift, 2021

Different post‐weld treatment methods have been developed to enhance the fatigue strength of welded steel structures and extend the service lives of their components. High‐frequency mechanical impact (HFMI) treatment and tungsten inert gas (TIG) remelting are two methods that have attracted considerable interest in recent decades. This paper presents the results of a study of fatigue life extension for pre‐fatigued welded steel details which can be achieved using HFMI treatment and TIG remelting. More than 250 fatigue test results were collected – including different details such as butt welds, longitudinal attachments, transverse attachments and cover plate attachments. HFMI treatment was found to extend the life considerably when the specimens treated were free from cracks or when existing cracks were < 2.25 mm deep. TIG remelting could extend fatigue lives even with cracks > 4 mm deep. In comparison to TIG remelting, HFMI treatment results in a longer fatigue life extension for pre‐fatigued details, provided existing cracks are < 2.25 mm deep. Regarding TIG remelting, the depth of possible remaining cracks was found to be a substantial parameter when assessing the degree of life extension.

experiments

analysis and design

Steel bridges

TIG remelting

fatigue life extension

pre‐fatigue

high‐frequency mechanical impact

allowable crack size

Författare

Hassan al-Karawi

Chalmers, Arkitektur och samhällsbyggnadsteknik, Konstruktionsteknik

Mohammad al-Emrani

Chalmers, Arkitektur och samhällsbyggnadsteknik, Konstruktionsteknik

Steel Construction

1867-0520 (ISSN) 1867-0539 (eISSN)

Vol. 14 2 95-106

LifeExt - Livslängdsförlängning för befintliga stålbroar

Trafikverket (TRV 2018/27547), 2018-05-15 -- 2020-11-30.

VINNOVA (2017-02670), 2017-06-08 -- 2019-12-31.

Drivkrafter

Hållbar utveckling

Ämneskategorier

Materialteknik

Samhällsbyggnadsteknik

Bearbetnings-, yt- och fogningsteknik

Annan materialteknik

Styrkeområden

Building Futures (2010-2018)

Materialvetenskap

Infrastruktur

Chalmers materialanalyslaboratorium

DOI

10.1002/stco.202000053

Mer information

Senast uppdaterat

2021-06-24