KCl induced corrosion of a 304-type austenitic stainless steel at 600 degrees C; The role of potassium
Artikel i vetenskaplig tidskrift, 2005

The influence of KCl on the oxidation of the 304-type (Fe18Cr10Ni) austenitic stainless steel at 600 degrees C in 5% O-2 and in 5% O-2 + 40%H2O is investigated in the laboratory. The samples are coated with 0.1 mg/cm(2) KCl prior to exposure. Exposure time is 1-168 h. Uncoated samples are exposed for reference. The oxidized samples are analyzed by ESEM/EDX, XRD and AES. The results show that small additions of potassium chloride strongly accelerate high temperature corrosion, the oxide thickness being up to two orders of magnitude greater after exposure in the presence of KCl. The rapid corrosion is initiated by the formation of potassium chromate through the reaction of KCl with the protective oxide. Chromate formation is a sink for chromium in the oxide and leads to a loss of its protective properties. The resulting rapidly growing scale consists of an outer hematite layer with embedded K2CrO4 particles and an inner layer consisting of spinel oxide, (Fe,Cr,Ni)(3)O-4. Little or no chlorine is found in the scale or at the scale/metal interface.

oxidation

11-percent

breakaway corrosion

high-temperature corrosion

fired boilers

oxide hydroxide evaporation

KCl

deposits

chromate

alloys

chromium steel

water-vapor

oxidation

deposit

304L

chloride

flow-rate

Författare

Jesper Pettersson

Chalmers, Kemi- och bioteknik, Oorganisk miljökemi

Henrik Asteman

Chalmers, Kemi- och bioteknik, Oorganisk miljökemi

Jan-Erik Svensson

Chalmers, Kemi- och bioteknik, Oorganisk miljökemi

Lars-Gunnar Johansson

Chalmers, Kemi- och bioteknik, Oorganisk miljökemi

Oxidation of Metals

0030-770X (ISSN) 1573-4889 (eISSN)

Vol. 64 1-2 23-41

Ämneskategorier

Materialteknik

Kemi

DOI

10.1007/s11085-005-5704-3

Mer information

Senast uppdaterat

2018-10-15