Oxidation behavior of a Mo(Si,Al)2 composite at 900–1600 C in dry air
Artikel i vetenskaplig tidskrift, 2012

The oxidation of a Mo(Si,Al)2-based composite is investigated in the temperature range 900–1600 C in dry air. Exposure time was 72 h. Comparisons are made with the oxidation behavior of a conventional MoSi2-based material. Cross-sections are examined with scanning electron microscopy and transmission electron microscopy; the phase composition is analyzed by X-ray diffraction and convergent beam electron diffraction. The material forms a continuous external a-alumina scale throughout the temperature range. Below the scale, there is a continuous Mo5(Si,Al)3 layer that overlies Mo(Si,Al)2 in the bulk. The Mo(Si,Al)2 phase immediately beneath the Mo5(Si,Al)3 layer is depleted in Al. No indications of MoO3 volatilization could be found for the Mo(Si,Al)2 material

molybdenum disilicide

high temperature

oxidation

Författare

Linda Ingemarsson

Chalmers, Kemi- och bioteknik, Oorganisk miljökemi

Kristina M Hellström

Chalmers, Kemi- och bioteknik, Oorganisk miljökemi

Sead Canovic

Chalmers, Kemi- och bioteknik, Oorganisk miljökemi

Torbjörn Jonsson

Chalmers, Kemi- och bioteknik, Oorganisk miljökemi

Mats Halvarsson

Chalmers, Teknisk fysik, Mikroskopi och mikroanalys

Chalmers, Teknisk fysik, Materialens mikrostruktur

Lars-Gunnar Johansson

Chalmers, Kemi- och bioteknik, Oorganisk miljökemi

Jan-Erik Svensson

Chalmers, Kemi- och bioteknik, Oorganisk miljökemi

Journal of Materials Science

0022-2461 (ISSN) 1573-4803 (eISSN)

Vol. 48 4 1511-1523

Ämneskategorier

Oorganisk kemi

Materialteknik

Drivkrafter

Hållbar utveckling

Styrkeområden

Energi

Materialvetenskap

Fundament

Grundläggande vetenskaper

DOI

10.1007/s10853-012-6906-0