Comprehensive study of Mn–Fe–Al oxygen-carriers for chemical-looping with oxygen uncoupling (CLOU)
Artikel i vetenskaplig tidskrift, 2015

The reactivity and attrition resistance of Mn–Fe oxygen carriers with addition of Al2O3 as support have been investigated. Spray-dried oxygen-carrier particles with Mn:Fe molar ratios of 80:20 and 33:67 were prepared using different amounts of Al2O3. Each material was calcined for 4 h at 950 °C, 1100 °C or 1200 °C. The oxygen carriers were studied in a batch fluidized bed reactor to investigate their reactivity with wood char, CH4, syngas and also their oxygen release in N2. In order to measure the mechanical stability of the different materials, the attrition resistance was measured in a jet-cup apparatus. Addition of Al2O3 to materials with a Mn:Fe molar ratio of 80:20 was not advantageous. Generally oxidation of these materials was problematic. The Al2O3 supported materials with a Mn:Fe molar ratio of 80:20 calcined at 950 °C and 1100 °C showed poor attrition resistance and were highly fragmented or turned to dust, whereas those calcined at 1200 °C showed high attrition resistance but poor gas conversion.Materials with a Mn:Fe molar ratio of 33:67 supported with Al2O3 generally showed better attrition resistance. Also their oxidation with 5 vol% of oxygen was possible at temperatures higher than 850 °C. Furthermore, some of these materials showed good reactivity with methane, syngas and char. Low attrition, good reactivity and CLOU properties in combination with potentially low raw materials costs, make these materials interesting for CLC.

Iron manganese oxide

Al2O3

Chemical-looping combustion

CO2 capture

Chemical-looping with oxygen uncoupling

Författare

Golnar Azimi

Kemi och kemiteknik, Energi och material, Oorganisk miljökemi

Tobias Mattisson

Chalmers, Energi och miljö, Energiteknik

Henrik Leion

Kemi och kemiteknik, Energi och material, Oorganisk miljökemi

Magnus Rydén

Chalmers, Energi och miljö, Energiteknik

Anders Lyngfelt

Chalmers, Energi och miljö, Energiteknik

International Journal of Greenhouse Gas Control

1750-5836 (ISSN)

Vol. 34 12-24

Drivkrafter

Hållbar utveckling

Ämneskategorier

Materialteknik

Kemiteknik

Styrkeområden

Energi

Materialvetenskap

DOI

10.1016/j.ijggc.2014.12.022