Thermomechanical capacity of wheel treads at stop braking: A parametric study
Artikel i vetenskaplig tidskrift, 2018

During tread braking, the treads of railway wheels are subjected to a complex loading due to combined rolling contact and thermally induced stresses. In revenue traffic the running mode of the train varies and the operational parameters will influence the life of the wheels. To prevent excessive damage, it is therefore important to understand at which operational conditions wheel damage becomes unacceptable. The current study aims to find limits for tread braking with respect to the influence of thermal stresses on rolling contact fatigue (RCF) of the wheel tread when subjected to repeated stop braking. A parametric study, using 3D FE simulations and involving operational parameters such as axle load, maximum vehicle speed, deceleration, brake block material and initial wheel temperature, is carried out for a new wheel with an S-shaped web. Additional analyses investigate impact from wheel geometry by studying a wheel with a straight web and a wheel with a thin (worn) rim. The effects of simultaneous thermal loading from wheel–block frictional contact during braking and mechanical loading, due to the traversing wheel–rail rolling contact, are studied in an uncoupled thermomechanical analysis. In the wheel–rail contact simulations, frictional rolling contact stress distributions induced by braking are accounted for. Interfacial shear stresses and partial slip are also included in the model. A temperature-dependent elastoplastic model is utilised to characterise changes in material behaviour during braking. In the vicinity of the wheel tread, damage evolutions for the studied brake load cases are evaluated. The results show that high tread temperatures, in particular temperatures above 450 °C, have a strong detrimental influence on the RCF formation and, hence, also on the thermomechanical capacity of the wheel. On the other hand, it is found that for braking temperatures between 300 °C and 375 °C, the fatigue resistance is increased due to strain hardening effects. In addition, the parametric study points towards actual braking load cases that can give such temperatures in terms of initial speeds, axle loads, etcetera. Specifically, the study shows that the train axle load, that controls the normal wheel–rail contact force, has a substantial impact on the life of the wheel treads. Wheels having straight webs and S-shaped wheel web exhibit the same fatigue life of their treads, whereas a reduction in wheel rim thickness promotes ratchetting due to increased flexural stresses from the mechanical wheel–rail contact loading.

tread braking

elevated temperatures

ratchetting

railway wheel

rolling contact fatigue

finite element simulations

Författare

Mandeep Singh Walia

Chalmers, Mekanik och maritima vetenskaper, Dynamik

Ali Esmaeili

Chalmers, Industri- och materialvetenskap, Material- och beräkningsmekanik

Tore V Vernersson

Institutionen för mekanik och maritima vetenskaper, Dynamik

Roger Lundén

Chalmers, Mekanik och maritima vetenskaper, Dynamik

International Journal of Fatigue

0142-1123 (ISSN)

Styrkeområden

Transport

Materialvetenskap

Ämneskategorier

Teknisk mekanik

Annan materialteknik

Farkostteknik

Infrastruktur

C3SE (Chalmers Centre for Computational Science and Engineering)

DOI

10.1016/j.ijfatigue.2018.04.031