A versatile low-resistance ohmic contact process with ohmic recess and low-temperature annealing for GaN HEMTs
Artikel i vetenskaplig tidskrift, 2018

Deeply recessed ohmic contacts for GaN-based high electron mobility transistors (HEMTs) are demonstrated. It is shown that low-resistance ohmic contacts can be achieved with recessing beyond the AlGaN Schottky barrier where the ohmic contacts are formed on the sidewall of the recess. This makes the process versatile and relatively insensitive to the exact recess depth. The ohmic contact is based on a gold-free metallization scheme consisting of a Ta/Al/Ta metal stack requiring a low-temperature annealing. Important parameters for this type of ohmic contact process include the metal coverage, slope of the etched sidewall, bottom Ta-layer thickness, as well as annealing temperature and duration. The optimized contact resistance is as low as 0.24 Omega mm after annealing at 575 degrees C. Moreover, this sidewall contact approach was successfully implemented on different epitaxial heterostructures with different AlGaN barrier thickness as well as with and without AlN exclusion layer. All the samples exhibited excellent contact resistances in a wide range of recess depths. The Ta-based, sidewall ohmic contact process is a promising method for forming an ohmic contact on a wide range of GaN HEMT epitaxial designs.

sidewall contact

HEMT

ohmic recess

contact resistance

gold-free

GaN

Författare

Yen-Ku Lin

National Chiao Tung University Taiwan

Johan Bergsten

Chalmers, Mikroteknologi och nanovetenskap (MC2), Mikrovågselektronik

Hector Leong

Linköpings universitet

Anna Malmros

Mikrovågselektronik

Jr-Tai Chen

SweGaN AB

Ding-Yuan Chen

Chalmers, Mikroteknologi och nanovetenskap (MC2)

SweGaN AB

Olof Kordina

SweGaN AB

Herbert Zirath

Chalmers, Mikroteknologi och nanovetenskap (MC2), Mikrovågselektronik

Edward Yi Chang

National Chiao Tung University Taiwan

Niklas Rorsman

Mikrovågselektronik

Semiconductor Science and Technology

0268-1242 (ISSN) 1361-6641 (eISSN)

Vol. 33 9 095019

Ämneskategorier

Tribologi

Bearbetnings-, yt- och fogningsteknik

Annan materialteknik

DOI

10.1088/1361-6641/aad7a8

Mer information

Senast uppdaterat

2018-10-16