The influence of silicon on the corrosion properties of FeCrAl model alloys in oxidizing environments at 600 °C
Artikel i vetenskaplig tidskrift, 2018

The present study investigates the influence of Si on the high temperature corrosion behaviour of FeCrAl model alloys in O2, O2+H2O and O2+H2O + KCl at 600 °C for up to 168 h. The investigation by SEM/EDX showed that all alloys displayed a protective behaviour in dry O2. In the more corrosive environments (O2+H2O and O2+H2O + KCl) the addition of Si affected the oxidation properties in two ways; Alloys containing Si resisted breakaway oxidation caused by Cr-evaporation (O2+H2O) and the thickness of the oxide formed after breakaway oxidation decreased with increasing amount of Si (O2+H2O + KCl).

C. High temperature corrosion

A. Alloy

B. SEM

A. Aluminium

Författare

Johan Eklund

Chalmers, Kemi och kemiteknik, Energi och material, Oorganisk miljökemi

B. Jonsson

Kanthal AB

Amanda Persdotter

Chalmers, Kemi och kemiteknik, Energi och material, Oorganisk miljökemi

Jesper Liske

Chalmers, Kemi och kemiteknik, Energi och material, Oorganisk miljökemi

Jan-Erik Svensson

Chalmers, Kemi och kemiteknik, Energi och material

Torbjörn Jonsson

Chalmers, Kemi och kemiteknik, Energi och material, Oorganisk miljökemi

Corrosion Science

0010-938X (ISSN)

Vol. 144 266-276

Ämneskategorier

Annan materialteknik

Metallurgi och metalliska material

Korrosionsteknik

DOI

10.1016/j.corsci.2018.09.004

Mer information

Senast uppdaterat

2018-11-15