Vanadium recovery from steel converter slag utilised as an oxygen carrier in oxygen carrier aided combustion (OCAC)
Artikel i vetenskaplig tidskrift, 2021

This study investigates vanadium extraction from steel converter slag from the LD (Linz-Donawitz) process. This slag has been used as an active bed material in a biomass boiler in a combustion technique called oxygen carrier aided combustion (OCAC). This usage in the boiler could be compared to the roasting step in the common roasting-leaching method for vanadium extraction. Leaching of LD slag prior to use as an oxygen carrier is undesirable as the materials active in OCAC are removed. This study successfully leached the slag following use in the combustion process. Two methods of leaching were utilised to compare the OCAC slag against traditional methods of vanadium extraction; a continuous flow leaching procedure and a microwave-assisted leaching procedure. It was found that a vanadium extraction efficiency of 22.1% could be achieved from the OCAC slag using 5 M sulphuric acid as a leaching solution following 30 min water leaching followed by 30 min of continuous acid leaching. Using the microwave-assisted method and further optimising leaching conditions, a final efficiency of 49.1% was achieved with 4 M sulphuric acid and particle size within the range of 44–74 μm.

Microwave-assisted leaching

Continuous flow leaching

Oxygen carrier aided combustion (OCAC)

Vanadium leaching

Steel converter slags

Författare

Martin Attah

University of Strathclyde

Fredrik Hildor

Chalmers, Kemi och kemiteknik, Energi och material, Oorganisk miljökemi 2

Duygu Yilmaz

Chalmers, Kemi och kemiteknik, Energi och material, Oorganisk miljökemi 2

Henrik Leion

Chalmers, Kemi och kemiteknik, Energi och material, Oorganisk miljökemi 2

Journal of Cleaner Production

0959-6526 (ISSN)

Vol. 293 126159

Ämneskategorier

Analytisk kemi

Kemiska processer

Metallurgi och metalliska material

DOI

10.1016/j.jclepro.2021.126159

Mer information

Senast uppdaterat

2021-04-22